Meqathatso ea Nylon ea Mocheso e sebelisoang ho Windows
Sebopeho sa I, sebopeho sa C, sebopeho sa T, sebopeho sa CT le sebopeho sa HK ke sebopeho se tloaelehileng ka ho fetisisa, re ka boela ra latela litlhoko tsa bareki kapa litšoantšo ho iketsetsa sebopeho se seng se khethehileng.
1.Effectively e ile ea eketsa mocheso tsamaisong ea thepa ea thepa.
2.Reduces condensation ka fensetere.
3.Molumo o insulated.
4.Ntlafatsa boiketlo le boemo ba bophelo.
5.Possible double coatings ea mebala e fana ka phello e ntle ea botle bo botle.
6.Libopeho tse fapaneng li tla etsoa ho latela litlhoko tsa moreki.
7.Mocheso o sebetsang oa sekhahla sa mocheso oa mocheso ke 220 ° C, Melting Point e fihla ho 246 ° C.Sena se nolofalletsa ts'ebetso ea ho roala ka mor'a kopano ea li-profile tse kopantsoeng.
8.High corrosion-resistance, boemo ba leholimo-ho hanyetsa, ho hanyetsa mocheso, ho hanyetsa alkali le bophelo bo bolelele ba tšebeliso.
9.linear thermal dilation coefficient e batla e ts'oana le ea profiles tsa aluminium.
NO. | Ntho | Yuniti | GB/T 23615.1-2009 | Tlhaloso ea HC-Technical |
| Thepa ea Lintho | |||
1 | Botenya | g/cm3 | 1.3±0.05 | 1.28-1,35 |
2 | Mohala oa katoloso ea coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
3 | Vicat softening mocheso | ºC | ≥230ºC | ≥233ºC |
4 | Sebaka se qhibilihang (0.45MPa) | ºC | ≥240ºC | ≥240 |
5 | Ho etsa liteko tsa mapetsong a tsitsipano | - | Ha ho mapetsong | Ha ho mapetsong |
6 | Bothata ba lebopo | - | 80±5 | 80-85 |
7 | Matla a amang (a sa tsejoe) | KJ/m2 | ≥35 | ≥38 |
8 | Matla a tiileng (longitudinal) | MPa | ≥80a | ≥82a |
9 | Elasticity modulus | MPa | ≥4500 | ≥4550 |
10 | Elongation nakong ya khefu | % | ≥2.5 | ≥2.6 |
11 | Matla a ho tsikitlanya (transverse) | MPa | ≥70a | ≥70a |
12 | Mocheso o phahameng oa matla a ho kokobetsa (transverse) | MPa | ≥45a | ≥47a |
13 | Mocheso o tlase oa matla a ho tsikinyeha (transverse) | MPa | ≥80a | ≥81a |
14 | Matla a ho hanyetsa metsi (transverse) | MPa | ≥35a | ≥35a |
15 | Botsofali ba ho hanyetsa matla (transverse) | MPa | ≥50a | ≥50a |
1.Mohlala oa metsi a ka tlase ho 0.2% ka boima ba 'mele.
2.Maemo a tloaelehileng a laboratori:(23±2)ºC le (50±10)% mongobo o lekanyelitsoeng.
3. Litlhaloso tse tšoailoeng ka "a" li sebetsa feela ho I-shape strip ho seng joalo, litlhaloso tse fihletsoeng pakeng tsa mofani oa thepa le moreki ka lipuisano, li tla ngoloa ka konteraka kapa ka taelo ea theko.
Li-strip li tla bolokoa sebakeng se nang le moea o motlakase le o omileng, ho behoa ka mokhoa o holimo, ho ela hloko ho thibela metsi, ho boloka hole le mohloli oa mocheso, ho qoba khatello e boima le ho kopana le acid, alkali hammoho le solvent ea manyolo.
Re na le matla a tlhahiso ea limithara tse 100000 ka letsatsi.Bakeng sa litlhaloso tse tloaelehileng, re na le hlobo, 'me re tla romelloa ka matsatsi a 15-20 ka mor'a ho fumana depositi.